001x7 (732) water softener resin price sodium cation resin

001x7 (732) water softener resin price sodium cation resin

Pre treatment of Yang resin

The pretreatment steps for cation resin are as follows:

Firstly, use saturated saline solution, which is approximately twice the volume of the treated resin. Soak the resin in the saline solution for 18-20 hours, then drain the saline solution and rinse with clean water to ensure that the discharged water does not turn yellow;

Next, use a 2% -4% NaOH solution with the same amount as above, soak in it for 2-4 hours (or clean with a small flow rate), drain the alkaline solution, and rinse the resin until the discharged water is close to neutral;

Afterwards, use a 5% HCl solution with the same amount as above, soak for 4-8 hours, drain the acid solution, and drift with clean water until neutral for later use.

With the continuous increase in domestic market demand, we will further expand our production and sales scale while improving quality and increasing variety. We will continue to serve our customers both now and in the future. We sincerely welcome new and old customers to visit our company for inspection and work guidance. Let's work together to create tomorrow!

001x7 (732) water softener resin price sodium cation resin
For cation exchange resins, they can also be classified into styrene based resins and acrylic based resins based on the type of their matrix.

The structural characteristics include the use of strong acidic cationic resins, strong alkaline anionic resins, and the transition from H-type resins to Na type regeneration equipment.
The types of chemically active groups in resins determine their main properties and categories.

When H resin is converted to Cl type.
Firstly, it can be divided into two categories: cationic resin and anionic resin, which can respectively exchange ions with cations and anions in solution.

The volume of the resin gradually decreases, the porosity of the exchange agent layer gradually decreases, and the volume of the resin decreases by 80100mm when the resin fails.