Hot metal Analyzer

NegotiableUpdate on 05/11

Model

Nature of the Manufacturer: Producers

Product Category

Place of Origin

Online Consult

Overview

A molten iron analyzer is a specialized rapid-testing instrument used at the melting floor in the foundry industry. It is employed before molten iron is tapped from the furnace to quickly determine carbon and silicon content as well as carbon equivalent (CE); some models can also measure manganese, phosphorus, and sulfur. It guides charge calculation and adjustment of molten iron composition, helping prevent casting defects such as gas porosity, white-iron structure (chilling), shrinkage porosity, and excessive hardness. It is an essential furnace-front quality control device for every foundry.

Product Details

Technical Parameters And Functions

Instrument Specifications	Host	Brand-name Industrial personal computer	Working Temperature	0~40℃
	Monitor	15-inch TFT true color monitor	Working relative humidity	<80%
	Suitable power supply	AC220V 50Hz	Power consumption	40W
	Dimensions	410×450×280mm	Weight	10kg
Main Functions	Measurement functions	Carbon equivalent, carbon content, silicon content, magnesium content, spheroidization rate, tensile strength, Brinell hardness
	Calculation function	Calculate based on the component supplement amount automatically/manually
	Data storage function	Record data according to the measured time, and can record more than 1,000 measurement results.
	Data output function	optional USB port (U disk) or RJ45 interface (network cable interface) to transfer output data to other computers
	Historical record reproduction function	Historical measurement data and cooling curve chart reproduction
Measurement range and accuracy	Measurement item name	Measurement range	Measurement accuracy
	Carbon equivalent (CEL)	2.50%～4.80%	±0.08%
	Carbon content (C%)	2.30%～4.20%	±0.05%
	Silicon content (Si%)	0.60%～3.80%	±0.10%
	Manganese content (Mn%)	0.10%～1.40%	±0.15%
	Sphericization rate	60%~99%	±5%
	tensile strength	150～400MPa	±10MPa
	Brinell hardness	100~300HB	±10 HB