FZT 01054-2012 Test Method for Surface Friction Properties of Fabrics

Preface

This standard was drafted in accordance with the rules provided in GB/T1.12009.

This standard replaces FZ/T01054.21999 "Fabric Style Test Method - Surface Friction Test Method".

The main differences between this standard and FZ/T01054.21999 are as follows:

Revised the scope of application of the original standard and expanded the applicable product types of the new standard (see Chapter 1);

Added normative reference document clauses (see Chapter 2);

The term 'coefficient of variation of dynamic friction coefficient' in Chapter 2 of the original standard has been deleted;

Added Test Method A, with the test procedure from Chapter 7 of the original standard as Method B (see Chapter 7);

The selection of friction pressure, abrasive, and test speed for method B has been clarified (see 5.2).

This standard was proposed by the China National Textile and Apparel Council.

This standard is under the jurisdiction of the Basic Standards Subcommittee of the National Textile Standardization Technical Committee (SAC/TC209/SC1).

This standard was drafted by the National Textile Products Quality Supervision and Inspection Center, Dongli Fiber Research Institute (China) Co., Ltd., and Dongli Textile Testing Center.

The main drafters of this standard are Gong Yingqiu, Wang Baojun, Li Fangli, and He Xiaoxia.

The previous versions of the standards replaced by this standard are:

FZ/T01054.21999;

FJ552.21985。

Product Introduction

The PY-E612 microcomputer friction coefficient tester from Shenzhen Puyun Electronics Co., Ltd. is suitable for testing the surface smoothness of packaging and printing paper films. It detects the ratio of the frictional force between the two surfaces of the packaging paper and the test material to the vertical force acting on one surface. The friction performance of the material can be expressed by the dynamic and static friction coefficients of the material. The surface smoothness of packaging printing materials is tested by measuring their dynamic and static friction coefficients, in order to ensure smooth transportation and packaging on high-speed production lines and meet the requirements of high-speed product packaging.

The PY-E612 microcomputer friction coefficient tester is used to measure the static and dynamic friction coefficients of plastic films and sheets, rubber, paper, cardboard, woven bags, fabric styles, metal composite belts for communication cables and optical cables, conveyor belts, wood, coatings, brake pads, wipers, shoe materials, tires and other materials when sliding. By measuring the friction coefficient (or smoothness) of the materials, the production quality and process indicators of the materials can be controlled and adjusted to meet the requirements of product use. In addition, it can also be used for measuring the smoothness performance of daily chemical products such as cosmetics and eye drops.

According to the standard:

GB/T 17200、GB/T 22895、ISO 8295、ASTM D1894、TAPPI T816、GB/T 2792

Technical parameters of friction coefficient meter:

1. Coefficient measurement range: 0~1

2. Test force accuracy: ر 0.001N

3. Measurement range: 0~10N

4. Weight of slider: 200 ± 2 g

5. Slide size: 63 × 63mm

6. Journey: 10+60mm (GB 10006, ISO 8295), 150mm (ASTM D1984)

7. Sliding speed: 100mm/min (GB 10006, ISO 8295), 150mm/min (ASTM D1984) stepless speed regulation

8. Other speeds: (0~550) mm/min adjustable

9. Maximum size of specimen: upper specimen 63 × 63mm, lower specimen 80 × 200mm

10. Sample thickness: ≤ 2mm

11. Workbench size: 100 × 500mm

12. Dimensions: 640x310x200mm

13. Weight: Approximately 25kg